Pvc Sheet For Waterproofing
The idea of waterproofing buildings is becoming more and more significant, and as a result, waterproof material development is never stopping. PVC sheet is a kind of double-colored plastic composite film that is pressure-formed from a high polymer material and has a polyester reinforcing layer sandwiched in the middle for waterproofing. It is perfect for waterproofing roofs since it contains anti-slip grooves on the surface and an anti-fouling coating on the top layer that is unaffected by UV light or weather.
- Fast Delievery
- Quality Assurance
- 24/7 Customer Service
Product Introduction
The idea of waterproofing buildings is becoming more and more significant, and as a result, waterproof material development is never stopping. PVC sheet is a kind of double-colored plastic composite film that is pressure-formed from a high polymer material and has a polyester reinforcing layer sandwiched in the middle for waterproofing. It is perfect for waterproofing roofs since it contains anti-slip grooves on the surface and an anti-fouling coating on the top layer that is unaffected by UV light or weather.
This waterproofing PVC sheet can be used in conjunction with rock wool insulation board and put immediately to the current roof surface without needing to be removed. It is straightforward to fix in the future and works well with steel plate and concrete roofs.
The building process is quick, produces less trash, and emits less carbon dioxide. Because of its exceptional performance, PVC sheet is widely employed in a variety of waterproofing applications. PVC waterproofing sheets are widely utilized in the construction and industry sectors for a variety of purposes, including roofs, subterranean civil defense projects, landfills, subways, tunnels, bridges, airports, granaries, and numerous venues.
PVC waterproofing sheets are highly effective and frequently utilized in a variety of waterproofing applications. It is extensively utilized in a wide range of subterranean and roof-related civil defense projects, landfills, subways, tunnels, bridges, airports, granaries, and other industrial and construction-related locations. PVC sheet waterproofing is a great option for roofing waterproofing due to its high practicality and simplicity of installation.
Landfills, subways, tunnels, Bridges, airports
Various roofing and underground civil defense projects
Industrial and construction sectors
Fratures
Long-term plasticity, recyclable nature, non-toxicity, innocuousness, and stability in size and color all contribute to green environmental protection.
Great heat and age resistance, long-term weather resistance, self-extinguishing from fire, and exceptional low temperature flexibility.
Effective resistance to dangerous chemicals, erosion from industrial pollutants, wear resistance, and joints created by hot air welding to create a body that is sturdy, dependable, and long-lasting.
Convenient construction: low cost, good plasticity, appropriate for detailed treatment, flexible construction technology selection based on base surface and duration, and convenient maintenance.
The surface is smooth, easy to clean, and conducive to the dispersion of water vapor (closed moisture can be released via the coil without forming blisters).
UV and solar radiation protection, compliance with LEED certification standards for green buildings, exposed use, lack of a protective layer, and a reasonable service life of up to 25 years or longer.
Specification
|
Product Name |
Thickness (mm) |
Width (mm) |
Length (m) |
|
PVC sheet membrane for waterproofing |
1.2, 1.5, 2.0 |
2.0 |
20 |
Technical Data
|
Item |
Indes |
|||
|
homogeneous |
underlying with fabric |
reinforced with mesh |
||
|
Flexibility at low temperature |
-2.5℃, no cracking |
|||
|
Water tightness |
0.3mpa, 2h, water tight |
|||
|
Impact resistance |
0.5kg.m, impermeable |
|||
|
Lap seam peeling strength |
4.0 or membrane breakage |
3.0 |
||
|
Right-angled tear strength |
50 |
- |
- |
|
|
Trapezoid tear strength |
- |
150 |
250 |
|
|
Water absorption (70℃, 168h), % |
After immersion≤ |
4.0 |
||
|
After drying≤ |
-4.0 |
|||
|
Heat aging (80℃) |
Period, h |
672 |
||
|
Appearance |
No bubbling, crack, layered, bonding and hole |
|||
|
Retention rate at max. Tension, %≥ |
- |
≥85% |
≥85% |
|
|
Retention rate at max Tensile strength, %≥ |
≥85% |
- |
- |
|
|
Elongation retention rate at max tension, %≥ |
- |
- |
≥85% |
|
|
Elongation retention rate at break, %≥ |
≥85% |
≥85% |
- |
|
|
Flexibility at low temperature |
-20℃, no cracking |
|||
|
Chemical Resistance |
Appearance |
No bubbling, crack, layered, bonding and hole |
||
|
Retention rate at max. Tension, %≥ |
- |
≥85% |
≥85% |
|
|
Retention rate at max Tensile strength, %≥ |
≥85% |
- |
- |
|
|
Elongation retention rate at max tension, %≥ |
- |
- |
≥80% |
|
|
Elongation retention rate at break, %≥ |
≥80% |
≥80% |
- |
|
|
Flexibility at low temperature |
-20℃, no cracking |
|||
|
Artificial weathering aging |
Period, h |
1500 |
||
|
Appearance |
No bubbling, crack, layered, bonding and hole |
|||
|
Retention rate at max. Tension, %≥ |
- |
≥85% |
≥85% |
|
|
Retention rate at max Tensile strength, %≥ |
≥85% |
- |
- |
|
|
Elongation retention rate at max tension, %≥ |
- |
- |
≥80% |
|
|
Elongation retention rate at break, %≥ |
≥80% |
≥80% |
- |
|
|
Flexibility at low temperature |
-20℃, no cracking |
|||
|
The Hydrostatic resistance is only applicable for the pressed roofing. |
||||
|
The period for the artificial weather aging test is 2500h for single ply roofing system. |
||||
|
The artificial weather aging test does not need for the membrane of unexposed use. |
||||
Hot Tags: pvc sheet for waterproofing, China pvc sheet for waterproofing suppliers, factory, customized logo PP PE waterproofing membrane, best waterproofing membrane for bathrooms, butyl rubber sheet waterproofing, felt waterproofing membrane, polyguard 650 waterproofing membrane, best waterproofing membrane for decks